Products Advantages
● Neutral curing, does not corrode the substrate. ●No formaldehyde, no solvent, no smell. ●High strength and elasticity, impact resistance, fatigue resistance, and can directly bond objects. ●Temperature resistance range: -40℃~90℃, long-term use will not age. |  |
Products Parameters
Product Name | MS polymer sealant |
Density | 1.51±0.02 g/cm³ |
Shrinkage rate | ≤2% |
Skin Time | 5~20min |
Curing time | ≥2.5mm/24h |
Elongation at break | ≥400% |
tensile strength | ≥4.0MPa |
100% Tensile strength | ≥1.8MPa |
Hardness Shore A | 50~60 |
Pear Strength | ≥3.0 N/mm |
Shrinkage rate after curing | ≤1.5% |
Peel Strength | ≥5.0 N/mm |
| Packing | 280ml/300ml/600ml. |
| Color | White, Black, Grey etc. |
| Quantity/carton | 24 cartridges/20 sausages. |
Application Scenarios
It is mainly used for pasting and fixing various large-area components and various plates, and can continuously maintain high-strength bonding to materials such as stainless steel, aluminum alloy, plastic, glass, ceramic tile and wood.
Products Advantages
● Neutral curing, does not corrode the substrate. ●No formaldehyde, no solvent, no smell. ●High strength and elasticity, impact resistance, fatigue resistance, and can directly bond objects. ●Temperature resistance range: -40℃~90℃, long-term use will not age. | |
Products Parameters
Product Name | MS polymer sealant |
Density | 1.51±0.02 g/cm³ |
Shrinkage rate | ≤2% |
Skin Time | 5~20min |
Curing time | ≥2.5mm/24h |
Elongation at break | ≥400% |
tensile strength | ≥4.0MPa |
100% Tensile strength | ≥1.8MPa |
Hardness Shore A | 50~60 |
Pear Strength | ≥3.0 N/mm |
Shrinkage rate after curing | ≤1.5% |
Peel Strength | ≥5.0 N/mm |
| Packing | 280ml/300ml/600ml. |
| Color | White, Black, Grey etc. |
| Quantity/carton | 24 cartridges/20 sausages. |
Application Scenarios
It is mainly used for pasting and fixing various large-area components and various plates, and can continuously maintain high-strength bonding to materials such as stainless steel, aluminum alloy, plastic, glass, ceramic tile and wood.